Scientists have uncovered a critical mechanism behind battery failure in solid-state batteries, providing new insights that could help unlock safer, longer-lasting energy storage technologies. Every time a smartphone is charged or an electric vehicle is plugged in, billions of lithium ions move through a battery to store energy.
Future devices could perform far better with solid state batteries, a technology that promises longer-lasting phones, safer energy storage, and electric vehicles capable of traveling much farther on a single charge.
Yet one stubborn problem has kept these batteries from reaching the mainstream: tiny structures called dendrites that can destroy a battery from the inside. Now, researchers at the Max Planck Institute for Sustainable Materials (MPISusMat) have uncovered exactly how these microscopic defects trigger battery failure.
Their findings, published in Nature, provide new insight into one of the most important challenges facing next-generation energy storage. Unlike conventional lithium ion batteries, which rely on a liquid electrolyte to move ions between electrodes, solid-state batteries use a solid ceramic electrolyte.
Eliminating the liquid component offers several advantages. Solid-state designs can potentially store more energy in the same amount of space, reduce fire risks, and remain functional for longer periods.
The technology has attracted enormous interest from automakers and electronics manufacturers because it could dramatically improve battery performance.
In theory, smartphones could go days without charging, while electric vehicles could achieve driving ranges up to three times greater than current models. Despite those advantages, solid-state batteries face a surprising weakness.
During charging, needle-like dendrites can grow from the lithium anode and extend into the solid electrolyte. If they reach the opposite electrode, they create an internal short circuit that can rapidly disable the battery. What has puzzled scientists is how lithium, a soft metal, can penetrate and fracture a ceramic material that is far harder and more rigid.
The widely use of solid-state batteries is till now prevented due to the formation of dendrites while charging. “Although the electrodes and the forming dendrites consist of lithium metal, which is soft like a gummy bear, the dendrites are able to penetrate the ceramic electrolyte and lead to a short circuit,” said Dr. Yuwei Zhang, lead author of the study and head of the ‘Chemo-Mechanics of Battery Materials’ group at MPISusMat.
“How can soft dendrites fracture the stiff solid ceramic? There are two hypotheses: either internal stress is built up inside the dendrites and induces mechanical fracture of the solid electrolyte. Or, electrons leak along the grain boundaries of the solid electrolyte promoting the formation of lithium nuclei that interconnect later.”
To determine which explanation was correct, the researchers developed an extensive experimental approach that allowed them to study the materials under vacuum and at cryogenic temperatures. These conditions prevented contamination from oxygen and moisture while also minimising unwanted effects from electron microscopy.